Fabrication and characterization of bolus material using polydimethyl-siloxane

Abstract

Bolus has been used in radiotherapy to reduce tissue harm and to increase the superficial dose for skin cancer treatment. Commonly, a bolus is made of melamine in several hospitals. In this research, polydimethyl-siloxane (PDMS) material was used for bolus fabrication. The aims of the study are to investigate bolus density, percentage surface dose and its structural strength for each various composition. In bolus preparation, bolus material used composition variation between PDMS volume and catalyst volume. Composition variation were 20:1, 22:1, 24:1, 26:1, 28:1, 30:1 and 32:1. PDMS and catalyst were mixed by chemical solution deposition method. Bolus was molded by using glass cast with the size of 10 × 10 × 0.5 cm3. Bolus density was analyzed by mass per volume equation, for bolus radiation was examined by the linear accelerator using two electron energy (5 and 7 MeV) and bolus strain and tensile strength were examined by Brookfield CT 3 machine. The results of bolus density were similar with soft tissue density, while the lowest and highest density each variation are 22:1 and 28:1. In general, the use of bolus has increased the surface dose. Percentage of surface dose at 5 MeV energy is higher than 7 MeV energy. The highest percentage of surface dose at 5 MeV energy with 0.5 and 1.0 cm bolus thickness was achieved at composition of 32:1. For strain and tensile strength result, the lowest and highest strain each variation are 22:1 and 28:1, then the lowest and highest tensile strength each variation are 32:1 and 28:1. These results is important to select composition material for bolus fabrication in radiotherapy treatment.