Abstract
Polyimide (PI) aerogel has surfaced in research and development as a result of its heat resistance, flame retardancy, and low dielectric constant. However, it is still a challenge to reduce the thermal conductivity while improving its mechanical strength and retaining hydrophobicity. Herein, the PI/thermoplastic polyurethane (TPU) composite aerogel was synthesized by coupling TPU with PI via a novel method of chemical imidization combined with freeze-drying technology. With this technique, PI aerogel with excellent comprehensive performance is produced. Interestingly, the volume shrinkage of the composite aerogel decreased from 24.14 to 5.47%, which leads to low density (0.095 g/cm3) and elevated porosity (92.4%). In addition, strong mechanical strength (1.29 MPa) and high hydrophobicity (123.6°) were achieved. More importantly, PI/TPU composite aerogel demonstrated a low thermal conductivity of 29.51 mW m-1 K-1 at ambient temperature. Therefore, PI/TPU composite aerogel can be a promising material for hydrophobic and thermal insulation applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.