Fabrication and Characterization of (100),(001)-Oriented Reduction-Resistant Lead-Free Piezoelectric (Ba,Ca)TiO3 Ceramics Using Platelike Seed Crystals

Abstract

The preparation of reduction-resistant (Ba,Ca)TiO3 ceramics as lead-free piezoelectric materials was studied. To improve their electrical properties, (100),(001)-oriented (Ba0.85Ca0.15)TiO3 ceramics were fabricated by the reactive templated grain growth method using a mixture of platelike CaTiO3 and BaTiO3 particles. The platelike CaTiO3 and BaTiO3 particles were prepared through a topochemical microcrystal conversion process using CaBi4Ti4O15 and BaBi4Ti4O15 plate-like precursor crystals. The 100 orientation degree of the grain-oriented (Ba0.85Ca0.15)TiO3 ceramics was 92%, as estimated by Lotgering's equation. In addition, 1 mol % Ba excess and 1 mol % Mn-doped (Ba0.85Ca0.15)TiO3 sintered bodies, which were sintered at 1350 °C in an Ar flow containing H2 (0.3%), had sufficient resistivity to allow the characterization of electrical properties. The ferroelectric and field-induced strain properties of the (Ba0.85Ca0.15)TiO3 ceramics, sintered in the reducing atmosphere, were markedly improved as a result of fabricating grain-oriented samples. The field-induced strain coefficient (estimated from the slope of the unipolar strain loop) of the nonreducible (100),(001)-oriented (Ba0.85Ca0.15)TiO3 ceramics reached 570 pm/V, which was higher than that of polycrystals (260 pm/V) with no preferential orientation.