Abstract
14H LPSO phase seriously affected dynamic recrystallization (DRX) behavior of extruded Mg92Gd3Zn1Li4 alloy. After hot extrusion, extensive DRXed grains took place at kink boundaries, while only a few of DRXed grains were formed at original grain boundaries. The formation of DRXed grains near kink boundary was beneficial for mechanical properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.