Abstract
We have extended the applicability of the photoluminescence method after electron irradiation for quantifying low-level C impurities in Si crystals. The intensity ratio of the G-line to the intrinsic emission normalized by the ratio of the reference sample is used as an index of the C concentration. The calibration curves have already been established for Czochralski-grown crystals with resistivity higher than 50 Ω·cm (n-type) and higher than 5 kΩ·cm (p-type). We showed that the method was extendable to the resistivity range down to 30 Ω·cm in n-type samples with the O concentration in the range 1–6 × 1017 cm−3. The extension to float-zone (FZ) crystals was realized by using the theoretical relationship between the C concentration and the G-line intensity ratio normalized by the ratio of the FZ reference sample. Regarding the extension to conductive p-type B-doped samples, the formation of B-related radiation-induced defects was found to be an obstacle.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.