Abstract
In this study, a new explosive welding method provided an effective way for manufacturing ITER-grade 316L(N)/CuCrZr hollow structural member. The welding parameters (stand-off distance and explosion rate) were calculated respectively using equivalent frontal collision wave model and effective energy model. The welded samples were subject to two step heat treatment cycles (solution annealing and aging). Optical microscopy (OM) and scanning electron microscopy (SEM) were utilized to analyze the microstructure of bonding interface. The mechanical properties of the welded samples were evaluated through microhardness test and tensile test. Moreover, the sealing property of the welded specimens was measured through helium leak test.Microstructural analysis showed that the welded sample using effective energy model had an ideal wavy interface. The results of microhardness test revealed an increase in hardness for both sides near to the bonding interface. And the hardening phenomenon of interface region disappeared after the solution annealing. SEM observation indicated that the samples with the post heat treatments exhibited a ductile fracture with dimple features after tensile test. After the specimens undergo aging strengthening, there was an obvious increase in the strength for all specimens. The helium leak test results have proven that the welded specimens are soundness.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.