Abstract
This work reports enhancing the hard magnetic properties of a binary ferromagnetic Heusler alloy based on Mn-Al system through mechanical milling. We report the processing induced evolution of magnetic properties for two sets of alloys, both having the same stoichiometric composition of Al-55at.%Mn with one of them containing high temperature ε phase while the other consisting of only metastable ferromagnetic τ phase. No effect of milling on the magnetic properties of ε phase could be detected due to its nonmagnetic nature. However, subsequent annealing at 350°C for 30min after milling results in structural change and exhibits magnetic response. The phase transitions were found to depend on prior milling history. The highest saturation magnetization and coercivity were obtained for 4h milled sample that is annealed at 350°C for 30min with values of 23emu/g and 5.2 KOe, respectively. In the case of samples with initial microstructure consisting of grains of only metastable τ phase, no decomposition could be observed when milled for a period up to 9h. Additionally, it was observed that after 3h of milling, the saturation magnetization value reduces to 24emu/g and coercivity increases to 5.2 KOe from an initial values of 116emu/g and 0.98KOe respectively. Further milling causes a decrease in both the values. Annealing of the 3h milled powder at 350°C for 30min, resulted in a slight decrease in coercivity (Hc=4.9 KOe) while a significant increase in saturation magnetization (34emu/g) value could be observed. Experimental results suggest that magnetization reversal is domain nucleation controlled and that the nonmagnetic phases (β+γ2) present can act as the pinning sites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.