Abstract
Currently, researchers are giving much more attention to carbon allotropes for hydrogen storage applications. SWCNT-(Mg–Ti) composites have been synthesized by the ball milling technique. The XRD patterns confirmed the solid solution formation of Ti in Mg. The substitution of SWCNT in Mg–Ti intermetallic alloy increases the dislocation density to 8.2x10−3nm−2 and reduces the crystal size from 46 to 28 nm and lattice strain of 0.54 to 0.28 %. The Raman analysis confirmed the existence of SWCNTs by presenting D and G bands and also confirmed the vibrations of Mg–Ti alloy. After the substitution of SWCNT, the exothermic peak reduced from 232 °C to 210 °C. The activation energy is also reduced after the substitution of SWCNT; it drastically reduces the activation energy to 66.59 kJ/mol for Mg67Ti29SWCNT4 alloy among the prepared samples. The impedance spectroscopy shows a higher diffusion coefficient of 5.2488x10−11 cm2s−1 for SWCNT substituted Mg–Ti alloy compared to pristine alloy. The hydriding/dehydriding studies were observed on the developed electrode material and Mg67Ti29SWCNT4 delivered a maximum storage capacity of 826 mAhg−1.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.