Exploring the effect of radiation crosslinking on the physico‐mechanical, dynamic mechanical and dielectric properties of EOC–PDMS blends for cable insulation applications

Abstract

This work focuses on the effect of electron beam irradiation on the physico‐mechanical, dynamic mechanical and dielectric properties of blends based on ethylene octene copolymer (EOC) and poly dimethyl siloxane (PDMS) rubber. It is found that electron beam irradiation caused considerable improvement in the physico‐mechanical properties; the tensile strength was enhanced by nearly 35% for 70:30 EOC:PDMS blend. Phase morphology of the blends analyzed before irradiation by scanning electron microscopy (SEM) exhibited droplet/matrix morphology with sizes of the PDMS rubber domain varying from 0.55 µm to 0.47 µm as the amount of PDMS rubber decreased from 30 wt% to 10 wt%. This reduction in the PDMS rubber domain has been correlated with the physico‐mechanical properties of the blends. Further, the dynamic mechanical properties and creep behavior of these EOC:PDMS blends before and after irradiation has been studied. It is inferred that the 70:30 blend after radiation crosslinking shows a 17% decrease in the creep compliance, i.e. higher creep resistance compared to neat blends. All the radiation crosslinked blends exhibited lower dielectric constant, lower dielectric loss and higher electrical resistivity as compared to the virgin blends which makes it suitable for cable insulating application. Copyright © 2016 John Wiley & Sons, Ltd.