Abstract
Many surface modification technologies have been developed on biomedical magnesium (Mg) and its alloys to expand potential clinical applications. In this study, the bio-safe manganese (Mn) element was implanted into the biomedical Mg surface by a metal vapor vacuum arc (MEVVA) technique. In the Mn-implanted layer, Mn existed in the form of both metallic and oxidized states. Besides, Mn ion implantation changed the corrosion behavior of biomedical Mg in Hank’s solution. At the initial stage of immersion, the corrosion rate was accelerated owing to the galvanic couple between metallic Mn and Mg, and micro-scale galvanic corrosion was uniformly distributed on surfaces. With the immersion time prolonging, Mn-implanted Mg displayed enhanced anti-corrosive property, presenting as a change from corrosion prone to corrosion resistance. On the one hand, the anti-corrosive and uniform Ca, P-containing products were formed on the corroded surface based on uniformly-distributed micro-scale pitting corrosion. On the other hand, the metallic Mn tended to be oxidized to stable Mn oxide so that galvanic corrosion was retarded. This research attempts to explore the effect of Mn ion implantation on the corrosion behavior of biomedical Mg, and offers new insight into novel surface modifications of biomedical Mg devices for long-time implantation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.