Abstract
Three new quaternary Zintl phases with the "9-4-9" formula, Ae9Mn4-xAlxSb9 (Ae = Ca, Yb, Eu), have been synthesized using Pb as the metal flux, and their crystal structures have been established by single-crystal X-ray diffraction. Both Ca9Mn2.91(4)Al1.09Sb9 and Yb9Mn3.59(6)Al0.41Sb9 are isostructural with Ca9Mn4Bi9, and they crystallize in the orthorhombic space group Pbam with unit cell dimensions of a = 12.4571(8), 12.2884(16) Å, b = 22.1352(16), 22.024(3) Å, and c = 4.6012(3), 4.6187(6) Å, respectively. Their anionic structures can be viewed as infinite ribbons based on corner-shared tetrahedrons. Also, Eu9Mn2.87(4)Al1.13Sb9 has the space group Cmca and a = 9.4883(7) Å, b = 23.6895(18) Å, and c = 24.4845(19) Å. The structural relationships between Ca9Mn2.91(4)Al1.09Sb9 and Eu9Mn2.87(4)Al1.13Sb9 are compared and discussed as well. The successful Al3+ substitution provides additional electrons to the compounds to achieve structural stability. Magnetic susceptibility and electrical resistivity measurements, performed on single crystals of Eu9Mn2.87(4)Al1.13Sb9, indicate complex magnetic properties and semiconductor behavior. The physical properties of Yb9Mn3.59(6)Al0.41Sb9 are similar to those observed for Yb9Mn4.18(2)Sb9.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.