Abstract
Nanoscale metallic multilayer (NMM) films are systems offering insight into the role of interfaces in metal plasticity, deformation, and strengthening mechanisms. Magnetron sputtering was used to fabricate the Ta/Cu NMM films with a periodicity (equal Ta and Cu layer thickness) from 6 to 80 nm, and with the structure exhibiting immiscible tetragonal β-Ta and face-centred cubic Cu phases. Transmission electron microscopy and X-ray diffraction analyses revealed that, irrespective of the period, all films manifested a polycrystalline structure. The growth direction of both Cu and Ta layers was found to be along 〈001〉 β-Ta || 〈111〉 Cu directions, with the crystallite size constrained by the layer thickness. The studies showed that the Ta/Cu NMMs exhibited compressive residual macro-stress and flow strength, and enhanced elastic recovery at the periodicity of ≤12 nm. Activation volume V⁎ value of 11 to 20 b3 as determined from the indentation creep test under a constant load, may indicate a mixed deformation mechanism. This mechanism likely involves the emission of dislocations from the incoherent Ta/Cu interfaces, as well as the formation of screw dislocations within Cu grains. The high-load indentation test, TEM studies, and the rCLS model collectively demonstrate that all NMM films predominantly undergo plastic deformation. This plastic deformation primarily occurs within the soft Cu layer, while the propagation of dislocations across the incoherent interface is largely excluded.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.