Exploring growth conditions and Eu2+ concentration effects for KSr2I5:Eu scintillator crystals II: Ø 25 mm crystals

Abstract

Europium doped potassium strontium iodide is a very promising scintillator for national security applications due to its ease of growth and excellent scintillation properties. For this work the fast crystal growth and scintillation properties of 1-inch diameter single crystals of KSr2I5:Eu2+ (KSI:Eu) were investigated. We focused our efforts on optimizing the growth parameters required to produce one-inch diameter crystals without decreasing the previously reported fast pulling rate of 5 mm/h. Cracking was minimized by replacing the quartz ampoules with carbon coated quartz ampoules; thus, several crack free single crystals of KSI with varying Eu2+ concentrations were grown, including a Ø 1″ by 6″ long boule with 2.5% Eu.The maximum achievable performance of each crystal was measured using small 0.012 cm3 specimens. The volumetric dependencies of the light yield, energy resolution and decay time were evaluated using KSI:Eu 2% specimens with volumes ranging from 0.012 cm3 to 18 cm3. For large volumes (≥ 9 cm3), the performance was comparable to other high performing scintillators, with light yields up to 78,200 ph/MeV and energy resolutions as good as 3.2% at 662 keV. The initial version of a hermetic package has been developed, and the stability of the sealed crystal is promising.