Abstract
This manuscript includes structural, optical, photoluminescence, and thermoluminescence behaviors of Terbium incorporated CaWO4 samples with nominal compositions of Ca1-xTb2x/3WO4 (x = 0.01, 0.02, 0.03, 0.04, 0.05) prepared by the traditional solid-state reaction route. Results found from the Rietveld refinements of X-ray diffraction patterns confirmed that all the samples have tetragonal crystal structures with I41/a space group. The variation of unit cell volume with the compositions shows an anomaly at x = 0.03. Band gap energy values of these synthesized samples are found from the UV–Visible absorbance spectra with increasing order. Photoluminescence behaviors, as well as the FWHM values, are analyzed from the excitation along with the emission spectra. Critical quenching concentration at x = 0.03 with a critical energy transfer distance of ∼ 20 Å caused by the dipole-dipole interactions is found in these spectra. CIE Chromaticity coordinates are indicated the green emission color of all the prepared samples with high color purity, correlated color temperature, color rendering index, and luminous efficiency of radiation values. Quantum efficiency of the material with x = 0.03 Tb concentration is observed under 255 nm excitation wavelength. PL decay analyses of the phosphors are carried out and the average lifetime values are calculated. Thermoluminescence spectroscopy of x = 0.03 irradiating by 15 min of UV dose is described as the lower UV dosimetry and second-order kinetics of the material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.