Experiments and theory on pentacene in the thin film phase: structural, electronic, transport properties, and gas response to oxygen, nitrogen, and ambient air

Abstract

We investigated the morphological, structural, electronic, and transport properties of pentacene thin films grown by vacuum thermal evaporation on different inert substrates at room temperature. The results of our atomic force microscopy (AFM), X-ray diffraction and scanning tunnelling microscopy (STM) analysis show a structure in the so called “thin film phase” with 1–2 μm sized grains. Atomic terraces are clearly evidenced with AFM and give an inter-planar spacing of 1.54 nm corresponding to the (001) distance. The Scanning Tunneling Spectroscopy measurements show an HOMO–LUMO gap of 2.2 eV. After vacuum thermal evaporation on patterned substrates with different inter-electrodes distances, we have performed in situ measurements of the electrical response of such thin films. We found for these films a resistivity of ρ = 4.7 ± 0.2 · 10 4 Ω m, that is an order of magnitude lower than the value reported to date in literature for single crystals of pentacene. This value is not affected by the presence of grain boundaries. The resistivity is further reduced by a factor 8.9 ± 0.7, 14 ± 1, 2.3 ± 0.3 upon exposure to oxygen, nitrogen and ambient air, respectively. In addition density functional theory calculations have been performed to investigate the electronic structure of pentacene in this specific phase, focusing on the effects on the relevant electronic properties of the relative orientation of the molecules within the crystalline unit cell, so far experimentally unknown. Our results show that the energy bandwidth and band-gap are crucially affected by the molecular stacking. Furthermore, by comparing our theoretical spectra with the scanning tunneling spectroscopy (STS) measurements, we propose a molecular arrangement that gives a good agreement with experiments as far as the relevant orbitals are concerned. For this polymorph, we find a HOMO and LUMO bandwidth of ≈ 0.7 eV and ≈ 0.8 eV, respectively, which are significantly larger than those obtained for the pentacene bulk-phase and are consistent with the larger conductivity experimentally observed in pentacene thin films.