Abstract
In this study, investigation has been made on the impact response of twill weave carbon fabric/epoxy foam sandwich composites by subjecting two types of stacking sequences of a sandwich composite structure, SC1 and SC2 to quasi-static indentation and low velocity impact loading. SC1 and SC2 had a sequence of [0/90, ±45, Core, 0/90, ±45], [0/90, ±45, 0/90, ±45, 0/90, Core, 0/90, 0/90, 0/90, 0/90], respectively. This work was done by use of material testing system and an instrumented Drop-Weight Machine (CEAST 9350 drop tower). Foam sandwich composite structures are mainly used in making an Engine Hood. The analysis was done with increase of impact energy on both types of stacking sequences, until complete perforation of the specimens at 25 Joule impact energy occurs. The failure processes of the damaged specimens under the three different impact energies (5 J, 15 J, and 25 J) were evaluated by comparing load–displacement curves. Images of damaged samples were taken from both impacted side and non-impacted side and compared for all impact energies. Cross-sections of damaged specimens were also inspected visually and discussed. The load-displacement curves were obtained to characterize the failure mechanisms in the face sheets and core. Failure modes were also studied by sectioning the samples at the impact location and observed under an optical microscope. The primary damage mode was found due to the fiber fracture, delamination, matrix crack, and foam crack.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.