Abstract
To improve the poor characteristics of low strength and high compressibility of weak silty soil, a series of samples with different cement dosage, fiber content, and fiber length was prepared in this experiment, and unconfined compressive strength (UCS) tests, triaxial tests, and scanning electron microscopy (SEM) tests were carried out to explore the influence of polypropylene fiber on the strength of cement-stabilized soil and analyze the curing mechanism of fiber-reinforced cement soil. The test results show that the factors affecting the UCS of the sample from high to low were: cement dosage, fiber content, and fiber length. An orthogonal test found that the optimal ratio of the sample was cement dosage of 18%, fiber content of 0.4%, and fiber length of 3 mm, and the UCS of the sample can reach 1.63 MPa. The triaxial test shows that when the cement dosage is 15% and the fiber length is 9 mm, the incorporation of fiber can significantly improve the toughness and strength of soil. When the cement dosage is 15%, the UCS with 0.4% fiber content is 1.6 times that without fiber. With the increase of fiber content, the peak stress and axial strain of fiber-cured soil are increased, and the cohesion and internal friction angle are also increased. The failure mode and SEM test of fiber-reinforced cement soil show that when the cement dosage is 15% and the fiber length is 9 mm, the addition of fiber can improve the deformation ability of cement soil and slow down the development of cracks. With the increase in fiber content, the number and width of cracks are significantly reduced, and the failure mode changes from brittle failure to ductile failure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.