Abstract
ABSTRACT Hydrogen fluoride (HF) corrosion of boiler water-cooled wall pipes at high temperature hinders the co-disposal of fluorinated hazardous wastes and coal by combustion. In this paper, common water-cooled wall pipes (15CrMoG and 20G) were utilized to perform gaseous HF corrosion experiments at high temperature on a horizontal tube furnace. The effects of temperature on HF corrosion of different water-cooled wall pipes in 0.2% HF were investigated. Corrosion kinetics curve was obtained by calculating the mass increase due to corrosion. The microscopic morphology and physical phase composition of water-cooled wall pipes after HF corrosion were analyzed. The corrosion resistances of the two water-cooled wall pipes decrease with increasing the temperature. The corrosion weight gain curves of 15CrMoG and 20G at 550 ℃ are ΔW 1.9144 = 0.2100t and ΔW 1.8356 = 0.1344t, respectively. The average corrosion rates of 15CrMoG and 20G are 0.0177 and 0.0125 mg/(cm2·h), respectively. The corrosion resistance of 15CrMoG is superior compared to 20G. The HF corrosion at high temperature consists of non-alternating fluorination and oxidation of the metal matrix. This study is of great significance for the protection of boilers with HF corrosion at high temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.