Experimental Study on Flow-Front Fingering Instabilities in Injection Molding of Polymer Solutions and Melts

Abstract

An experimental investigation of the flow behavior of dilute, semi-dilute and concentrated polymer solutions has been carried out to gain a better understanding of the underlying mechanisms leading to the occurrence of instabilities at the advancing flow front during the filling of a mold cavity. Experiments were performed using various mass concentrations of low and high molecular weight polyacrylamide polymers in corn syrup and water. This paper reports a new type of elastic fingering instabilities at the advancing flow front that has been observed only in semi-dilute polymer solutions of high molecular weight polymers. These flow front elastic instabilities seem to arise as a result of a mixture of widely separated high molecular weight polymer molecules and low molecular weight solvent molecules, which gives rise to a largely non-uniform polydisperse solution, with respect to all the kinds of molecules in the resulting mixture (solvent molecules and polymer molecules). The occurrence of these instabilities appears to be independent of the injection flow rate and the cavity thickness. Moreover, these instabilities do not manifest themselves in dilute or concentrated regimes, where respectively, polymer molecules and solvent molecules are minor perturbation of the resulting solution. In those regimes, smooth flow fronts are confirmed from our experiments. Based on these findings, the experimental investigations have been extended to polymer melts. Different mixtures of polycarbonate melts of widely separated molecular weights (low and high molecular weights) were first prepared. The effect of the large polydispersity of the resulting mixtures on the flow front behavior was subsequently studied. The same instabilities at the flow front were observed only in the experiments where a very small amount of high molecular weight polycarbonate polymer has been mixed to a low molecular weight polycarbonate melt (oligomers).