Abstract
Low cycle and high cycle fatigue tests of 35CrMo steel at different pretorsional angles were conducted and cyclic hardening and softening curves, hysteresis loops and S-N curves were obtained of 35CrMo steel after the torsional prestrain. Scanning electron microscopy (SEM) analysis was also made of the fatigue fracture. The results show that: 35CrMo steel features obvious cyclic softening with basically the same law and degree at different torsional prestrains. The area surrounded by the stress-strain hysteresis loop decreases with the increment of the pretorsional angle; the torsional prestain reduces the fatigue life of the materials.