Abstract
In petrochemical and petroleum refining industries, the hydrogenation technology is widely used. As materials used in key equipment, such as hydrogenation reactors, are subjected simultaneously to the action of hydrogen and high temperature, studies on material property degradation and remaining life predicting are of very important engineering and academic significance. An in-service test block from the hydrogenation reactor DC101A was divided and tested. Material properties of 2.25Cr–1Mo steel after service of about 10 5 h at the operating pressure of 17.12 MPa and temperature of 427 °C were obtained, including the embrittlement status of the aged material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.