Abstract
This paper concerns the experimental study of damage of ITER divertor plasma-facing components (PFCs) under a combination of pulsed plasma heat loads (representative of controlled ITER type I edge-localized modes (ELMs)) and quasi-stationary heat loads (representative of the high heat flux (HHF) thermal fatigue expected during ITER normal operations and slow transient events). The PFC's tungsten armor damage under pulsed plasma exposure was driven by (i) the melt layer motion, which leads to bridges formation between neighboring tiles and (ii) the W brittle failure giving rise to a stable crack pattern on the exposed surface. The crack width reaches a saturation value that does not exceed some tens of micrometers after several hundreds of ELM-like pulses. HHF thermal fatigue tests have shown (i) a peeling-off of the re-solidified material due to its brittle failure and (ii) a significant widening (up to 10 times) of the cracks and the formation of additional cracks.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.