Abstract
Over the years, many studies have been conducted to study and analyze the grain structures of metal alloys during additive manufacturing to improve mechanical properties. In particular, columnar grains are observed predominantly during rapid solidification of molten metal. This leads to lower mechanical properties and requires expensive secondary heat-treatment processes. This study is aimed at disrupting the formation of columnar grain growth during rapid solidification using ultrasonic vibration and analyzes the effects on grain structure and mechanical properties. A gas-metal arc welder mounted on a Rep-Rap-based low-cost metal 3 Dimension printer was used to deposit ER70S-6 mild steel layers on a plate. A contact-type ultrasonic transducer with a control system to vary the frequency and power of the vibration was used. The effects of ultrasonic vibration were determined from the statistical analysis of microstructure and micro-indentation techniques on the deposited layer and heat-affected zone. It was found that both frequency and interaction between frequency and power had significant impact on the refinement of average grain size up to 10.64% and increased the number of grains by approximately 41.78%. Analysis of micro-indentation tests showed that there was an increase of approximately 14.30% in micro-hardness due to the applied frequency during rapid solidification. A pole diagram shows that application of vibration causes randomization of grain orientation. Along with the results from this study, further efforts in modeling and experimentation of multi-directional vibrations would lead to a better understanding of disrupting columnar grains in applications that use mechanical vibrations, such as welding, directed energy deposition, brazing, etc.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.