Abstract
In the present study, Ti–6Al–4V alloy was bonded to electrolytic copper at various temperatures of 875, 890 and 900°C and times of 15, 30 and 60min through diffusion bonding. 3MPa uniaxial load was applied during the diffusion bonding. Interface quality of the joints was assessed by microhardness and shear testing. Also, the bonding interfaces were analysed by means of optical microscopy, scanning electron microscopy and energy dispersive spectrometer. The bonding of Ti–6Al–4V to Cu was successfully achieved by diffusion bonding method. The maximum shear strength was found to be 2171N for the specimen bonded at 890°C for 60min. The maximum hardness values were obtained from the area next to the interface in titanium side of the joint. The hardness values were found to decrease with increasing distance from the interface in titanium side while it remained constant in copper side. It was seen that the diffusion transition zone near the interface consists of various phases of βCu4Ti, Cu2Ti, Cu3Ti2, Cu4Ti3 and CuTi.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.