Abstract

Objective: Endodontic perforation is a challenging mishap that should be repaired with a biocompatible material, Mineral trioxide aggregate (MTA) and Biodentine are the most commonly used repair materials. However, these materials are expensive, (MTA) has prolonged setting time and difficult manipulation. The purpose of this study is to prepare the experimental nano calcium-aluminate/tri-calcium-silicate (CA/C3 S) material and comparing its physical properties with biodentine and MTA, to evaluate the experimental material eligibility to compete the commercial repair materials. And to perform part two (animal study) that will evaluate the cytotoxicity, the biocompatibility and the efficacy of (CA/C3 S) in furcal perforation repair compared to diode laser. Material and Methods: A mixture of calcium carbonate and aluminum oxide was used to formulate calcium aluminate phase (CA), tri-calcium-Silicate phase (C3 S) was formulated by firing of calcium carbonate and quartz. The produced powders were investigated by X-ray diffraction, then (CA) and (C3 S) mixed with water.(CA/ C3 S) compared with MTA and biodentine for setting-time, micro-hardness, dimensional-stability and solubility. Results: Mean setting time of (CA/C3 S) was (32.70±0.75min) which is significantly higher than MTA and Biodentine. The Mean microhardness of (CA/C3 S) was (56.50±7.41VHN) which has no statical difference with MTA and Biodentine. Solubility results showed weight increase for (CA/C3 S) as following (6.29±3.05)and loss of weight for MTA and Biodentine. The percentage of change in dimensions for(CA/C3 S) increased as following (0.64±0.78) while decreased for MTA and Biodentine. Conclusion: The experimental (CA/C3 S) material showed good microhardness, dimensional stability and acceptable setting time that could be improved in further work. KEYWORDS Biodentine; MTA; Nano calcium aluminate; Tri-calcium-silicate, Root repair.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call