Abstract
Split-cylinder fracture of fiber-reinforced ultra-high-performance concrete (UHPC) was examined using two complementary techniques: X-ray computed tomography (CT) and acoustic emission (AE). Fifty-mm-diameter specimens of two different fiber types were scanned both before and after load testing. From the CT images, fiber orientation was evaluated to establish optimum and pessimum specimen orientations, at which fibers would have maximum and minimum effect, respectively. As expected, fiber orientation affected both the peak load and the toughness of the specimen, with the optimum toughness being between 20% and 30% higher than the pessimum. Cumulative AE energy was also affected commensurately. Posttest CT scans of the specimens were used to measure internal damage. Damage was quantified in terms of internal energy dissipation due to both matrix cracking and fiber pullout by using calibration measurements for each. The results showed that fiber pullout was the dominant energy dissipation mechanism; however, the sum of the internal energy dissipation measured amounted to only 60% of the total energy dissipated by the specimens as measured by the net work of load. It is postulated that localized compaction of the UHPC matrix as well as internal friction between fractured fragments makes up the balance of internal energy dissipation.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.