Abstract
Reactor pressure vessel (RPV) is one of the key equipment for nuclear power plant, and long-term exposure to high temperature is an important factor causing its performance deterioration. Under core meltdown conditions, RPV steel experiences high temperature creep due to the In-Vessel Retention (IVR) mitigation measures. This paper aims to investigate high-temperature mechanical properties, especially for the creep behaviors of 16MND5 steel after thermal aging at 650 °C for 2000 h. The results showed that the yield stress and ultimate tensile strength of the 16MND5 steel are decreased, and the creep rupture time is rapidly shortened after thermal aging. The microstructure was analyzed by scanning and transmission electron microscopy (SEM, TEM). 16MND5 steel showed a typical bainitic phase before thermal aging. After 2000 h of thermal aging, the micro-grains were coarsened, and finally changed into a ferritic microstructure. Based on Larson-Miller (LM), Orr-Sherby-Dorn (OSD) parameters methods and Kachanov-Rabotnov (K–R) model to predict uniaxial creep life after thermal aging, the prediction results are satisfactory, and all within the double tolerance band. This work reveals the creep damage mechanism of 16MND5 steel after thermal aging, and provides basic data for the implementation of IVR strategy in nuclear power plants after long-term service.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Pressure Vessels and Piping
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.