Abstract
Abstract An experimental investigation was conducted to observe and analyze the microstructural evolution of phases present in the AK64 Al-Si-Cu alloy subjected to a modified T6 heat treatment (HT). The AK64 alloy1 is the Polish alternative of the A319.0 ASM standard aluminium alloy. The modified T6 HT schedule with a higher temperature and shorter duration was applied in the solutioning process and lower quenching and higher artificial ageing temperature than the prescribed by the ASM standard were used. The cooling curves registered during the liberating of overheating and solidifying processes give important information on nucleation temperatures for the Al dendrite network, Al-Si eutectic reaction and precipitation of Cu-rich phases. Comparison of the as-cast and heat treated microstructures revealed predicted microstructural changes and also partial fragmentation of the Fe-rich phases was observed after the application of the modified HT programme.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.