Abstract
The stabilities of the γ-(Co), γ′-Co3(Al,W), μ-Co7W6, β-CoAl and α-(W) phases in the Co-Al-W and Ni-Al-W ternary systems were investigated at 900, 1000, 1100 and 1300 °C. Electron probe microanalysis was used to determine compositions of the phases. Scanning electron microscopy was used to determine area fractions of the phases present after heat treatments. Thermodynamic modeling of the Co-Al-Ni-W quaternary system, using PandatTM software, was incorporated to determine relevant thermodynamic parameters for phases in the Co-rich region of the system. Phases were modeled using the substitutional solution model and compound energy formalism. Excellent agreement was found between experiments and thermodynamic modeling. This new thermodynamic database enables predictions of stable γ-γ′ compositions for a new class of high temperature, high strength Co-base superalloys.