Experimental Investigation and Thermodynamic Calculation of the Phase Equilibria in the Co-Cu-V Ternary System

Abstract

The phase equilibria of the Co-Cu-V ternary system at 900, 1000, 1100 and 1200 °C have been experimentally determined by optical microscopy and electron probe micro-analysis of the equilibrated alloys. The phase transformations were investigated by means of the differential scanning calorimetry. Based on the experimental data of phase equilibria and thermodynamic properties, the thermodynamic assessment of the Co-Cu-V ternary system was carried out by using the calculation of phase diagrams method. A consistent set of the thermodynamic parameters leading to reasonable agreement between the calculated results and experimental data was obtained in the Co-Cu-V ternary system. Meanwhile, the calculated results show that the critical temperature of metastable magnetically induced miscibility gap of (α f Co) and (α p Co) phases in the Co-V system gradually decreases with increasing Cu composition in the range of 0-3 wt.% additions.