Abstract
The stability of retained austenite is the most important parameter controlling the transformation plasticity effects in multiphase low alloy TRIP steels. In this work the thermodynamic stability of the retained austenite has been determined experimentally by measuring the Mσs temperature as a function of bainite isothermal transformation (BIT) temperature and time in two low alloy TRIP steels. A single‐specimen temperature‐variable tension test technique (SS‐TV‐TT) has been employed, which allowed to link the appearance of yield points in the stress‐strain curve with the mechanically‐induced martensitic transformation of the retained austenite. The results indicated that the MσS temperature varies with BIT temperature and time. Higher austenite stability is associated with a BIT temperature of 400°C rather than 375°C. In addition, the chemical stabilization of the retained austenite associated with carbon enrichment from the growing bainite is lowered at short BIT times. This stability drop is due to carbide precipitation and comes earlier in the Nb‐containing steel. At longer BIT times the retained austenite dispersion becomes finer and its stability rises due to size stabilization. The experimental results are in good agreement with model predictions within the range of anticipated carbon enrichment of the retained austenite and measured austenite particle size.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.