Experimental approach to investigate the constrained recovery behavior of coiled monofilament polymer fibers

Abstract

The aim of this work is to propose a new approach for investigating the thermo-mechanical behavior of coiled oriented polymer fibers with fixed ends and promote an understanding of the actuation response of coiled polymers in constrained recovery applications. In the proposed experimental methodology, a coiled fiber was pre-stretched by 50% and the distance between its ends remained constant, then it was subjected to a heating-cooling cycle ranging from 30 °C to 120 °C and the induced restoring force was measured. Based on these measurements, axial deformation and shear strain were obtained from full-field displacements extracted by the digital image correlation method from images of the coiled fiber. Three coiled fibers with different initial pitch angles were manufactured, and samples with lengths of 15 mm and 20 mm were tested. Bias angles and coil radius were also estimated using the experimental data associated with the helical spring theory. Results show that significant shape changes can be noticed above the glass transition temperature (47 °C), and these changes induce variation in the resultant forces. The effects of thermal softening and thermal contraction for a modest negative thermal expansion coefficient became evident at temperatures ranging from ∼47 °C to ∼90 °C, while the response of a coiled homochiral polymer fiber was achieved at temperatures close to 90 °C. During the cooling process, saturated states of the axial deformation and shear strain of the coiled fibers were observed at temperatures between 120 °C and 100 °C.