Experiment Study on Mechanical Performance of Shale Lightweight Aggregate Concrete

Abstract

High performance lightweight aggregate concrete is a kind of lightweight environment-protected building material with high strength, good workability, volume stability and durability, which is widely used in large scale engineering and some important engineering. In this paper water-binder ratio, fly ash content, pre-wetting time, sand ratio were tested to explore the comprehensive strength of lightweight aggregate concrete(LWAC). SEM was used to observe the microstructure characteristics of the specimens. The results showed that LWAC produced in the experiment present good performance, whose apparent density was 1760 Kg/m3～1930Kg/m3, 28d compressive strength was 55MPa～60MPa. Reasonable amounts of sand ratio(38%) and mineral admixtures(10%) were exited and the self-strength of lightweight aggregate played an important role in the preparation of LWAC. In the meanwhile, lightweight aggregates which were pre-wetted effectively increased the later strength.