Abstract
A flame retardant system based on expandable graphite (EG), aluminum diethylphosphinate (AlPI) and melamine polyphosphate (MPP) was investigated in glass fiber- (GF) reinforced polyamide 6 (PA6). Burning characteristics were evaluated via cone calorimeter, limiting oxygen index (LOI) and UL-94 tests. Thermogravimetric analysis (TGA) and coupled Fourier transform infrared spectroscopy (FTIR) was used to investigate the decomposition process as well as flame retardant modes of actions. Specifically, in the cone calorimeter tests, formulations containing EG showed excellent flame retardant properties for non-reinforced and reinforced PA6. The best performance was achieved for 25 wt.% glass fiber-reinforced PA6 containing solely 20 wt.% EG, corresponding to a measured pHRR of 134 kW/m2 and a total smoke production of 1.2 m2. Higher glass fiber contents of 45 wt.% (30 vol.%) revealed a lower char volume, which was attributed to both the limited space available for expansion and the sheer-induced reduction in particle size during processing. All of the reinforced PA6 formulations only achieved V2 classifications, but this was at low filling degrees (10 wt.%) for both net EG or EG/AlPi/MPP combinations. For GF-reinforced PA6 containing EG/AlPi/MPP mixtures, a synergistic effect was found to improve the oxygen index up to 30.6%.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.