Abstract
The amount of excess oxygen vacancies that are generated during FAST regime of direct-current flash sintering was estimated semi-quantitatively for 3 mol%–10 mol% Y2O3-doped ZrO2 (3–10YSZ) using the temperature dependence of the electrical conductivity. For the estimation, the electrical conductivity in the temperature range, where shrinkages are below a few percent, was used to avoid the effect of large microstructural changes on the electric conductivity. For all Y2O3 contents except 3YSZ, the amount of excess oxygen vacancies increased above a compact temperature of approximately 840 °C, which depended on Y2O3 content, and was highest in 8YSZ. Approximately 0.13% excess oxygen vacancy was generated by direct-current flashing in 8YSZ in the present electric field condition. In contrast, the increase in the excess oxygen vacancies is negligible in 3YSZ. The dependence of the amount of excess oxygen vacancies on the Y2O3 content was related possibly to the dependence of the electrode overvoltage on the Y2O3 content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.