Abstract
This study examined the corrosion resistance of the metallic paint-coated, uncoated, and damaged paint-coated form of the high-strength 6061 T6 Al alloy inside seawater. Solvent-based paint containing two different metallic pigments produced with an alkyd binder was produced and the coating of Al 6061 T6 alloy was made with this paint. To determine the course of corrosion electrochemical impedance spectroscopy method was used. Ecor and Rp values were calculated from potential and current change values. As a result, it was determined from the Ecor, Rp, SEM -EDX images, and Nyquist curves that the corrosion resistance of impact coatings was lower. The corrosion resistance of gold color paint substantially containing copper pigment was lower than that of silver color paint containing Al pigment was observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.