Abstract
Phosphate layers were prepared as the insulation coating for Fe and FeSiAl soft magnetic composites (SMCs) and mechanisms of the phosphating process have been investigated. Effects of high-temperature annealing on the phosphate coating and the magnetic properties of the SMCs have also been revealed. For Fe SMCs, the insulating coating mainly consists of iron phosphate after surface passivation. It degrades into iron phosphide after annealing at relatively high temperatures (600°C), leading to decreased electrical resistivity and increased eddy current for deteriorated magnetic properties of Fe SMCs. For the FeSiAl SMCs, the phosphate coating mainly contains Al(PO3)3, which converts into oxides such as Al2O3 and P2O5 after annealing. These oxides possess high electrical resistivity, and continue to serve as the insulation coating for the composites. Consequently, the resistivity of the FeSiAl SMCs increases with the annealing temperature, which is beneficial to decrease the eddy current loss for enhanced magnetic performance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.