Abstract
ABSTRACT12Cr ODS steel samples were prepared by mechanical alloying of the metal powders with 20-30 nm Y2O3 particles followed by isostatic pressing, hot rolling and final heat treatment. Evolutions of oxide particles such as YTaO4 and YCrO3 after each fabrication step were investigated by using TEM with EDS. Crystallographic correlation between oxide particles and the matrix was investigated in a HIPped sample, and interactions between dislocations and oxide particles were observed in hot rolled or heat treated sample. Size distributions of oxide particles were measured by carbon replica samples and it was found that coarsening of oxide particles from 9 to 12 nm occurred during hot rolling process. Additional isothermal annealing at 1250 ˚C revealed that phase transformation of oxide particles from monoclinic YTaO4 to face centered cubic Y3TaO7 was observed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.