Abstract
AbstractThe microstructural changes caused by various thermomechanical treatments were investigated for AISI 347 stainless steel. The high dislocation density which results from cold rolling is not annealed out even after long holding times at 600°C. When heating at higher temperatures, e.g. 750°C, precipitation of very fine NbC particles is observed, together with onset of recrystallisation. Complete recrystallisation resulting in equiaxed dislocation free grains occurs only when annealing severely cold worked specimens in the high temperature range of this investigation.MST/1708
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.