Abstract

The present investigation was carried out to examine the influence of austempering holding time on the microstructure and mechanical properties of low carbon, high silicon cast steels. Austempering treatment was carried out at a temperature of 400°C with varying holding time from 10 to 60min. The austempered microstructure showed the presence of bainite and retained austenite. The high carbon retained austenite was identified by X-ray diffraction and confirmed by transmission electron microscopy (TEM) analysis. It is observed that ultimate tensile strength (UTS) increased but percentage of elongation (%El) decreased with increasing austempering time. Increase in austempering time changed the morphology of bainite from fine to coarse lath. The carbide was formed when austempering time increased from 30min to 60min and resulted in decrease in ductility but increase in strength. The best combination of strength and ductility was observed at 400°C austempering temperature and 10–30min holding time. The fracture surface showed that dimple could not grow with increasing holding time and formation of carbide resulting in decreased ductility with increased holding time.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.