Abstract
In this paper, studied was the low carbon and low silicon (0.003%C,0.3%Si) cold-rolling steel sheet whose reduction ratio was 81% annealed at 870 °C in the laboratory salt-bath furnace and heated for 180s.The evolution of micro-orientations of grain coarsening at 1050°C and 1150°C on cold-rolling samples that were annealed at temperature 870°C and heated for 180s was studied by EBSD technology.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.