Abstract
The plastic deformation behavior of Ti–22.4Nb–0.73Ta–2Zr–1.34O alloy was investigated by compression testing at room temperature. The multi-peak stress oscillations of the true stress–strain curve, characterized by a stress plateau, initial strain-hardening, followed by strain-softening and a second strain-hardening stages, is observed in a titanium alloy for the first time. The experimental results show that the above four-stage plastic deformation behavior is caused by a change in the dominant deformation mechanisms. At the stress plateau stage, the alloy deforms via multiple plastic deformation mechanisms. The initial strain hardening is caused mainly by tangling of dislocations. Subsequent strain softening is due to the formation of kink bands. The second strain hardening corresponds to the formation of shear bands. The above results suggest that the dominant deformation mechanisms of Ti–Nb–Ta–Zr–O alloys are related not only to the stability of the β phase, but also to the extent of plastic deformation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.