Abstract
By performing short-term creep tests at 923K, the evolution of creep damage in a modified heat resistant steel and its oxide layer characteristic were investigated. Compared with conventional ferritic steels, the modified steel exhibited excellent short-term creep resistance. And the fracture mode remained transgranular under all test conditions. By analyzing creep data, high creep damage tolerance factors were obtained, indicating that precipitation coarsening should be the pronounced factor causing creep strain accumulation and the onset of tertiary creep stage. Combined with microstructural examination, it is found that the coarse precipitates at the prior austenite boundaries, mainly M23C6, contribute to the void formation and eventual transgranular failure. The oxide layers formed on the specimen surface consisted of Fe-rich [Fe,Cr]2O3 outer layer and Cr-rich [Fe,Cr]3O4 inner layer.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.