The thermal cyclic durability of a TBC is thought to be strongly dependent on the physical and mechanical properties of the bond coat layer. A novel high temperature microsample tensile testing technique has been employed to characterize the mechanical behavior of a platinum modified nickel aluminide bond coat at 0% and 28% of cyclic life in the temperature range of 25 to 1150 °C. Values for the coefficient of thermal expansion and the Young’s modulus are reported. The bond coat exhibits a ductile to brittle transition temperature at approximately 600 °C, and above this temperature the yield and creep strength decreases rapidly with temperature. A power law description of elevated temperature stress relaxation is developed. The intermediate temperature strength was found to increase with thermal cycling, while the high temperature strength remained the same. This evolution in properties has been related to the development of a martensitic transformation that occurs during each thermal cycle.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.