Abstract
A C-scan ultrasonic imaging system was used to investigate the microstructural evolution during dynamic recrystallization (DRX) of a 15Cr–15Ni–2.2Mo–Ti modified austenitic stainless steel (alloy D9). Four specimens were forged at 1273 K to different strains in the range 0.1–0.5. Specimens with true strains of 0.2 or lower did not show any variation in the amplitude of the first back-wall echo. However, a visible variation in the C-scan image was observed at and above the 0.3 strain level. This variation was attributed to the evolution of fine grains. The formation of fine grains was related to DRX, as indicated by electron backscattered diffraction. This study also revealed the characteristics of the DRX or ‘necklace grains’, as opposed to the so-called parent grains or rest of the microstructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.