Abstract
Microstructure evaluation of as-cast and annealed U–Zr (Zr=2, 6 and 10wt.%) alloys has been carried out for the first time using positrons as a probe. The chemical signature in the matter–antimatter annihilation gamma and the positron lifetime data suggests that majority of positrons are annihilating from Zr sites in the as-cast alloys. The results have been interpreted as due to the presence of Zr nano-agglomerates in the as-cast alloys which have a higher positron affinity as compared to the rest of the U matrix. A minimum agglomerate size of ∼2nm diameter has been calculated from the difference in positron affinity between the agglomerates and the matrix. Upon annealing, the Zr signature in the annihilation gamma photons vanishes suggesting that the Zr agglomerates diffuse out of U matrix and form micron-sized precipitates. This has been confirmed by scanning electron microscopy which shows a 3 times increase in the surface density of the precipitates in the annealed alloys as compared to the as-cast ones. Shorter positron diffusion length (measured using slow positron beam) as compared to precipitate separation has been invoked to explain the observed data.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.