Abstract

(1-x)(0.93Bi0.5Na0.5TiO3/0.07BaTiO3)-xCoFe2O4 ((1-x)BNT/BT-xCFO, where x = 0.1, 0.2, 0.3, 0.4 and 0.5) composite samples were synthesized by microwave assisted solid state reaction route and sintered at 1050 °C. X-ray diffraction study showed the presence of ferroelectric/ferromagnetic (FE/FM) phases without any peak of secondary phase. This was further confirmed by SEM study showing the presence of both FE/FM grains distinctly. Frequency dependent dielectric study showed maximum dielectric constant ("r) for the composite sample with x = 0.4. Polarization versus electric field (P-E) loop study revealed that maximum remnant polarization (2Pr = 1.75 μC/cm2) was found also for the 0.6BNT/BT-0.4CFO sample. Remnant magnetization (Mr) of the composite sample with x = 0.4 was found to be ∼7.81 emu/g. Magnetodielectric (MD) study of the 0.6BNT/BT-0.4CFO composite sample showed decrease in "r with the application of magnetic field and a MD effect of ∼2.4% (at 10 kHz) was found. Low leakage current value (∼10−4 A) was obtained in the 0.6BNT/BT- 0.4CFO composite sample. Change in piezoresponse force microscopy contrast after poling indicated on the changes in polarization of the ferroelectric domains. Reduction in Mr, observed in magnetic force microscopy contrast gave a clear evidence of presence of electric field induced magneto-electric (ME) coupling in the 0.6BNT/BT-0.4CFO composite sample.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.