Abstract
Inconel 706 is a newly developed superalloy, which offers high mechanical strength alongwith easy fabricability thus making it suitable for turbine disk applications. Although Inconel 706 exhibits a substantial increase in stress rupture and tensile yield strength compared to other superalloys, its conventional machining yields poor surface finish and low dimensional accuracy of the machined components. Hence, wire electrical discharge machining (WEDM) of Inconel 706 has been performed and various performance attributes such as material removal rate (MRR), surface roughness (SR), recast surface, topography, microhardness, microstructural and metallurgical changes of the machined components have been evaluated. The experimental results revealed that servo voltage, pulse on time, and pulse off time greatly influence the MRR and SR. Due to high toughness of Inconel 706, no micro cracks were observed on the machined surface. Micro voids and micro globules are significantly reduced at low pulse on time and high servo voltage. But, there is a propensity of thick recast layer formation at high pulse on time and low servo voltage. EDAX analysis of recast surface exposed the existence of Cu and Zn which have migrated from the brass wire. The subsurface microhardness was changed to 80μm due to significant thermal degradation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.