Abstract
It was attempted to assess nondestructively the degree of isothermal degradation of 2.25Cr-1Mo steel by using high frequency longitudinal ultrasonic wave. Microstructural parameter (mean size of carbides), mechanical property (Vickers hardness) and ultrasonic attenuation coefficient were measured for the 2.25Cr-1Mo steel isothermally degraded at 630°C for up to 4800 hours in order to find the correlation among these parameters. The ultrasonic attenuation coefficients at high frequencies (over 35MHz) were observed to increase rapidly in the initial 1000 hours of degradation time and then slowly thereafter, while the ones at low frequencies showed no noticeable increase. Ultrasonic attenuation at high frequencies increased as a function of mean size of carbides. Ultrasonic attenuation coefficient was found to have a linear correlation with the hardness, and suggested accordingly as a potential nondestructive evaluation parameter for assessing the mechanical strength reduction of the isothermally degraded 2.25Cr-1Mo steel.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.