Abstract
In this investigation, the oxidation of two-layer thermal barrier coatings (TBCs) prepared by EB-PVD (electron beam physical vapor deposition) in different oxygen concentration environments at 1323 K was evaluated by impedance spectroscopy and microstructural observation (SEM). The higher partial pressure of oxygen accelerated the oxidation rate of bond coating and faster oxidation caused cracking at interface between the TGO and the bond coat. Impedance spectroscopy was used to evaluate the microstructural changes which occurred in the TBC system non-destructively. The relationship between the electrical conductivity of the YSZ layer and its microstructure including the parameters of microcracks was established.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.